Inconel 800H Nickel Alloy Plate and Sheet UNS N08810 Alloy Thickness 0.3 - 30.0mm from TISCO BAOSTEEL
Products Specification
| Product Name | Nickel Alloy Plate & Sheet |
| Thinckness | Cold rolled:0.3mm-3mm Hot rolled: 3.0mm-30mm |
| Standard Size | Cold Rolled 1000*2000mm 1219*2438mm 1500*3000mm |
| Hot Rolled 1500*6000mm 1800*6000mm 2000*6000mm |
| Service | Cutting (laser cutting, plasma cutting, cutting machine), Bending, forged produce |
| Surface Service | Raw finishing (2B NO.1) Finishing(HL 8K Checkered.etc) |
| Standard | ASTM, AISI, DIN, EN, GB, JIS |
| Mainly Grade | ASTM Grade: Incoloy 800 / 800H ,Incoloy 825,Inconel 600 , Inconel 625 ,Inconel 718, Inconel690,Hastelloy B , Hastelloy B-2 , Hastelloy C276 , Hastelloy C4, Hastelloy C2000,
ASME Grade: N08800 N08810 N08825 N06600 N06601 N06690 N10001 N10665 N10276 N06455 N06625
EN 1.4588 2.4858 2.4817 2.4642 2.4617 2.4819 2.461 2.4856 |
| Brand | TISCO BAOSTEEL ZPSS LISCO JISCO |
Incoloy 800H Nickel Alloy
Incoloy 8Incoloy 800 H is an iron-nickel-chromium alloy having the same basic composition as Incoloy 800, with significantly higher creep rupture strength. The higher strength results from close control of carbon, aluminum and titanium contents in conjunction with a high temp anneal. The 800H modification was to control carbon (0.05 to 0.10%) and grain size to (>ASTM 5) to optimize stress rupture properties. Incoloy 800 H has further modifications to the combined titanium and aluminum levels (0.85 to 1.2%) to ensure optimum high temperature properties. The alloy is dual certified and combines the properties of both forms.
The chemical balance allows the alloy to exhibit excellent resistance to carburization, oxidation and nitriding atmospheres. 800HT will not become embrittled even after long periods of usage in the 1200-1600 deg F range where many stainless steels become brittle. Excellent cold forming characteristics typically associated with the nickel-chromium alloys are exhibited with 800HT. When cold formed extensively the grain size produces a visibly undulated surface called "orange peel". 800HT can be welded by the common techniques used on stainless steels.
Typical applications for the alloy include ethylene pyrolysis, hydrocarbon cracking, cracking furnaces for vinyl chloride, diphenol and acetic acid. The alloy is also used for valves, fittings and other components exposed to corrosive attack from 1100 to 1800 deg F.
Round bar ranging from 3/4" to 6" diameter, and light gauge sheet and plate. Incoloy 800 H material can be supplied in random lengths, cut to order or machined to customer requirementAs. Machining includes drilling, threading, milling, CNC shapes, turning, tapping, flanges and others.
Chemistry
Chemical Requirements |
| | Ni | Cr | Mn | C | Si | Fe | C |
| Max | 35.0 | 23.0 | 1.5 | 0.10 | 1.0 | | 0.75 |
| Min | 30.0 | 19.0 | | | | 39.5 | |
Tensile Data
Mechanical Property Requirements |
| | Ultimate Tensile, min. | Yield Strength (0.2% OS) | Elong. in 2 in. or 50mm (or 4D) min., % | R/A | Hardness |
| Min | 80 KSi | 35 KSi | 25 | | |
| Max | | | | | |
| Min | 550 MPa | 240 MPa | | | |
| Max | | | | | |
Specifications
| Form | Standard |
| Metal Type | UNS N08800 / N08810 / N08811 |
| Bar | ASTM B408 |
| Wire | |
| Sheet | ASTM B409 |
| Plate | ASTM B409 |
| Fitting | ASTM B366 |
| Forging | ASTM B564 |
| Weld Wire | |
| Weld Electrode | |