Titanium Round Bar Cold Drawn Bright Bar ASTM EN DIN JIS Standard Diameter 4 - 300mm
| Size | Dia.: 3 mm – 600 mm |
| Material | Gr.1, Gr.2, Gr.4, Gr.5, Gr.7, Gr.12, Gr.23, etc. |
| Standard | ASTM B348, ASTM F67, AMS 4928, ASTM F136,AMS 2631b, etc. |
| Surface | Black, Pickling, Sand-blasting, Polished |
| Condition | Cold rolled(Y), Hot rolled(R), Annealed (M), Quenching(C) |
| Shape | Square Bar, Round Bar, Hexagonal Bar, etc. |
Titanium bar is available produced and certified to Medical (ASTM F67, ASTM F136, ISO5832-2, ISO5832-3), Aerospace (AMS 4928, AMS 2631b), Industrial (ASTM B348) standards. Stock production is aligned to ASTM, AMS and ISO standards with other standards available on made to order.
Properties of titanium bar:
Titanium bar has Low Density and High Strength, Excellent Corrosion Resistance, Good resistance to effect of heat, Excellent Bearing to cryogenic property, Nonmagnetic and Non-toxic, Good thermal properties, Low Modulus of Elasticity.
Applications:
Titanium bar can be used in aircraft engines and parts, chemical equipment parts (reactors, pipes, heat exchangers and valves, etc.), ship hulls, bridges, medical implants, artificial bones, sporting products and consumer goods. Titanium bar is also used as titanium fasteners , such as titanium bolts nuts.
We can produce titanium bar according to customers’ drawing. Special requirements will be agreed on by the titanium suppliers and titanium buyers of negotiation. TigMetal bars for medical applications have tight tolerances and consistency in chemical composition, reducing machine set-up time and increasing cutting speeds. The excellent surface finish of TigMetal medical bars saves polishing time and contributes to a better end-product.
Chemical requirements (Nominal %)
| | N | C | H | Fe | O | Al | V | Pa | Mo | Ni | Ti |
| Gr 1 | 0.03 | 0.08 | 0.015 | 0.2 | 0.18 | / | / | / | / | / | bal |
| Gr 2 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | / | / | / | bal |
| Gr 3 | 0.05 | 0.08 | 0.015 | 0.3 | 0.35 | / | / | / | / | / | bal |
| Gr 4 | 0.05 | 0.08 | 0.015 | 0.5 | 0.4 | / | / | / | / | / | |
| Gr 5 | 0.05 | 0.08 | 0.015 | 0.4 | 0.2 | 5.5~6.75 | 3.5~4.5 | / | / | / | bal |
| Gr 7 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | 0.12~0.25 | / | / | bal |
| Gr 9 | 0.03 | 0.08 | 0.015 | 0.25 | 0.15 | 2.5~3.5 | 2.0~3.0 | / | / | / | bal |
| Gr12 | 0.03 | 0.08 | 0.015 | 0.3 | 0.25 | / | / | / | 0.2~0.4 | 0.6~0.9 | bal |
Mechanical requirements
| Grade | Tensil strength (min) | Yeild strength (min) | Elongation(%) |
| ksi | MPa | ksi | MPa |
| 1 | UNSR50250 | 35 | 240 | 20 | 138 | 24 |
| 2 | UNSR50400 | 50 | 345 | 40 | 275 | 20 |
| 3 | UNSR50550 | 65 | 450 | 55 | 380 | 18 |
| 4 | UNSR50700 | 80 | 550 | 70 | 483 | 15 |
| 5 | UNSR56400 | 130 | 895 | 120 | 828 | 10 |
| 7 | UNSR52400 | 50 | 345 | 40 | 275 | 20 |
| 9 | UNSR56320 | 90 | 620 | 70 | 438 | 15 |
| 12 | UNSR53400 | 70 | 438 | 50 | 345 | 18 |
Testing:
- Corrosion test
- Eddy Current test
- Mechanical test
- Microstructure test
- Ultrasonic test
Packaging:With the standard plastic bags inside, wooden case or as per client’s requirement.
Production process: Titanium Sponge—Compacting electrodes—Multiple melting—Titanium ingots—Machining—UT testing—Chemical composition inspection—Forged
billets—Forged/Rolled—Annealed—-Straightening—Machining—UT testing—Visual and Dimension Inspection—UT testing—Marking—Packaging—Delivery
Titanium bar is highly resistant to chloride-containing media, practically all salt solutions, seawater, a range of acids, organic and inorganic chemicals and gases. The high environmental resistance is primarily based on a very thin, tenacious and highly protective surface oxide film. The oxide film provides high resistance to erosion in high velocity process streams. It is non-magnetic and characterized by a high melting point, high strength-to-weight ratio and a low modulus of elasticity. We provide high quality titanium bar with competitive prices and unrivaled customer service.